Specifications:

For sealing pneumatic and hydraulic screw connections subject to high loads. With screw connections, up to the burst pressure of the pipe/hose

Excellent resistance to all hydraulic fluids and fuels
High degree of safety, as impairments due to breakdown are prevented.

Quick to harden, even at low temperatures
Minimum vehicle downtime.

100% sealing
Gaps are filled completely, so that the resulting bonding provides protection against corrosion from friction and protection against rust.

Resistant to a large number of bases, gases, solvents, oils and fuels

Silicone- and solvent-free

DOS system:

• Practical one-handed operation thanks to the clever turn lock

-You always have one hand free.

• Continuously adjustable dispensing system

-Dispensing can be adjusted to suit the application, and to keep consumption and costs to a minimum.

• No residue material in dispensing neck

-Costs optimised thanks to emptying with virtually no remaining product

Notice
The following plastics can be affected in the event of prolonged exposure: ABS, celluloid, polystyrene, polycarbonate (Macrolon), PMMA (Plexiglas), polysulfone, SAN (lurane, Tyril), Vinidur, vulcanised fibre and painted surfaces. We always recommend that you conduct your own tests.

The usage instructions are recommendations based on the tests we have conducted and are based on our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee the consistent quality of our products. We reserve the right to make technical changes and carry out further development.

Applications

Application area:
For sealing pneumatic and hydraulic screw connections subject to high loads. Specially designed for use with high pressure fluid systems in the automotive and commercial vehicle industry, metal and tool manufacturing, shipbuilding, machine and engine construction, electrical and electronics construction.

Instructions:
The surface must be free of oil, grease and other contaminants. The best adhesive results are achieved by first cleaning with metal cleaner 7063 (art. no. 0890107063). Observe flash-off time! Manually apply the product to the surface as a continuous bead or flat by screen printing. After sealing, close tightly as soon as possible, so that product does not build up and cause gaps. After assembly, the adhesive hardens to a viscoplastic. The cleaner the surface, the more secure the bonding. The hydraulic seal cures anaerobically, meaning that it only hardens where the adhesive has no contact with atmospheric oxygen. At the same time, the hardening speed is still being influenced by the catalytic effect of metal and the gap width. Excessive adhesive that is pressed out of the gap between the two parts will not harden and can be removed with a dry cloth or a cloth saturated with acetone cleaner (art. no. 0893460).

Passive materials: Nickel, zinc, tin, precious metals, aluminium with minimal copper and/or manganese content, high-alloy steel, oxide or chromate coats, plastic, glass and ceramic.
Active materials: Steel, brass, bronze, copper, aluminium (copper content greater than 1%)

Technical Information
Chemical basis: Methacrylic acid ether
Colour: Violet
Min./max. viscosity /conditions: 14000-20000 mPas / at 25°C, Brookfield RVT, spindle 5/2.5 rpm
Viscosity conditions: at 25°C, Brookfield RVT, spindle 5/2.5 rpm
Density: 1.2 g/cm³
Max. gap-filling ability: 0.15 mm
Suitable for: Thread diameter max. R 3/4 inch
Min./max. initial strength: 30-40 min
Min./max. functional strength: 2-3 h
Min./max. final strength: 12-24 h
Min./max. breakaway torque: 2-3 Nm
Breakaway torque conditions: M10 mm
Min./max prevail torque: 1-2 Nm
Conditions for prevail torque: M10
Min./max. compressive shearing strength: 1-3 N/mm²
Min./max. processing temperature: 5 to 35 °C
Min./max. temperature conditions: -55 to 150 °C
Min. flashing point: 100 °C
Shelf life from production/conditions: 12 Month / at room temperature
Weight of content: 50 g